KRAJ TERM

It is a high-strength heat-resistant concrete to all kinds of industrial applications, mainly for casings and construction elements.

Due to special chemical additives it needs a small amount of water to obtain a semi-liquid consistency. As a result it undergoes rapidly the process of heating the concrete wall.

By introducing three different types of fibers, the concrete achieves high resistance to temperature and mechanical shocks in the entire operating range from 0 up to 1350 °C.

KRAJ TERM

SCOPE OF APPLICATIONS 

– KRAJ TERM heat-resistant is suitable for all kinds of casings and walls in the operating conditions of 0 to 1350 °C in the presence of an abrasive medium in the exhaust gas.

 TECHNICAL DATA KRAJ TERM

REPROFILATION

Form

powder

Color

Grey/brown

Density of mortar

circa 2,2 g/cm3

Content of solid particles

100%

Consistency of mortar

Yielding/half-liquid
Temperature of use

+0 °C up to +1350 °C

Heat resistance

 up to 1350 °C

Compressive strength:

– after 24 h in 20 °C

– after 7 days in 20 °C

– after 28 days in 100 °C

– after burning in 800 °C

– after burning in 1000 °C

– after burning in 1350 °C

 

≥ 60 MPa

≥ 80 MPa

≥ 82 MPa

≥ 65 MPa

≥ 45 MPa

≥ 75 MPa

Alkali resistance

Very good
Density of concrete

2,18-2,20

Density after burning

1,80-1,90